ASTM 321 Stainless Steel Seamless Pipe , Polished Stainess SteelTube
321 Stainless Steel
A Titanium Stabilized Austenitic Stainless Steel with Excellent Resistance to Intergranular Corrosion After Exposure to Temperatures in the Chromium Carbide Precipitation Range of 800–1500°F (427–816°C)
Alloy 321 (UNS S32100) is a titanium stabilized austenitic stainless steel with good general corrosion resistance. It has excellentresistance to intergranular corrosion after exposure to temperatures in the chromium carbide precipitation range of 800–1500°F (427–816°C). The alloy resists oxidation to 1500°F (816°C) and has higher creep and stress rupture properties than alloys 304 and 304L. It also possesses good low temperature toughness. Alloy 321H (UNS S32109) is the higher carbon (0.04–0.10) version of the alloy. It was developed for enhanced creep resistance and for higher strength at temperatures
above 1000°F (537°C). In most instances, the carbon content of the plate enables dual certification. Alloy 321 cannot be hardened byheat treatment, only by cold working. It can be easily welded and processed by standard shop fabrication practices.
Weight % (all values are maximum unless a range is otherwise indicated)
| Element | 321 | 321H |
| Chromium | 17.00 min. –19.00 max | 17.00 min.–19.00 max. |
| Nickel | 9.00 min.–12.00 max. | 9.00 min.–12.00 max. |
| Carbon | 0.08 | 0.04 min.– 0.10 max. |
| Manganese | 2 | 2 |
| Phosphorus | 0.045 | 0.045 |
| Sulfur | 0.03 | 0.03 |
| Silicon | 0.75 | 0.75 |
| Titanium | 5 x (C + N) min.–0.70 max. | 4 x (C + N) min.–0.70 max. |
| Nitrogen | 0.1 | 0.1 |
| Iron | Balance | Balance |
Mechanical Properties
Typical Values at 68째F (20째C)
Yield Strength
0.2% Offset | Ultimate Tensile
Strength | Elongation
in 2 in. | Hardness |
| psi(min.) | (Mpa) | psi(min.) | (Mpa) | %(min.) | (max.) |
| 30,000 | 205 | 75,000 | 515 | 40 | 217 Brinell |
Hot FormingHot Forming
Working temperatures of 2100–2300°F (1149–1260°C) are recommended for forging, upsetting and other hot working processes. Do not work this alloy
at temperatures below 1700°F (927°C). Material must be water quenched or fully annealed after working to re-attain maximum corrosion resistance.
Cold Forming
The alloy is quite ductile and forms easily.
Welding
Alloy 321 can be readily welded by most standard processes. A post weld heat treatment is not necessary.
SINO Stainless Steel
-
SINO STEEL Professional inspection before dhipment of supplier's sample, including chemical and mechanical property.
-
MTC provided before shipment after order.
-
Strong safety ASTM,AISI, JIS, EN standards.
-
Third Party Inspection Packing inspection if customers need.
-
SINO STEEL With 10 years experience in stainless steel.
-
We provide slitting cutting, heat treatment, surface treatment, application consulting services.
-
All sizes could be customized in our warehouse.
-
We accept 100% L/C payment.
-
Just 2 hours to Shanghai port, the goods could be sent within 24 hours.
Any further Inquiry or question or Stainless Steel,Let SINO Know,always here for you,
Product Tags:
|
|
Titanium Stabilized Austenitic 321 Stainless Steel Pipe , Duplex Stainless Steel Pipe 6-630mm OD Images
|